  • Title: Chitosan-sodium alginate-based coatings for self-strengthening anticorrosion and antibacterial protection of titanium substrate in artificial saliva.
    Author: Duan Y, Wu Y, Yan R, Lin M, Sun S, Ma H.
    Journal: Int J Biol Macromol; 2021 Aug 01; 184():109-117. PubMed ID: 34119541.
    Abstract:
    A self-strengthening coating with silver nanoparticles (Ag NPs) doped chitosan (CHI) and sodium alginate (SA) polyelectrolytes was constructed on the surface of polydopamine (PDA) coated Ti substrate by a layer-by-layer assembly method. The PDA coating exhibited an excellent bond with Ti substrate, and also can uniformly deposit Ag NPs via a mild method without introducing any exogenous reductant. The CHI coating was assembled through a spin-coating method for controlling Ag+ release. The SA was introduced to enhance the anticorrosion performance by forming calcium alginate (CA) in a corrosive medium. The corrosion protection was investigated with electrochemical impedance spectroscopy and polarization curves tests in fluorine-containing artificial saliva. During immersion, the charge-transfer resistance and the protection efficiency (ŋ) presented a continuous increase with the immersion time, demonstrating that this coating possessed a remarkable self-strengthening capability, and the compositions of the outermost film changed from SA to CA with the Ca2+ cations of the corrosive medium as a crosslinker by SEM and EDS analysis. Furthermore, the ŋ remained up to 96.8% after immersion of 30 days, and then the coating also displayed a distinct inhibition zone on S. mutans. These results prove this coating possesses an excellent anticorrosion performance and antibacterial property.
    [Abstract] [Full Text] [Related] [New Search]