  • Title: Preparing Two-Dimensional Ordered Li0.33 La0.557 TiO3 Crystal in Interlayer Channel of Thin Laminar Inorganic Solid-State Electrolyte towards Ultrafast Li+ Transfer.
    Author: Lv R, Kou W, Guo S, Wu W, Zhang Y, Wang Y, Wang J.
    Journal: Angew Chem Int Ed Engl; 2022 Feb 07; 61(7):e202114220. PubMed ID: 34806279.
    Abstract:
    Inorganic superionic conductor holds great promise for high-performance all-solid-state lithium batteries. However, the ionic conductivity of traditional inorganic solid electrolytes (ISEs) is always unsatisfactory owing to the grain boundary resistance and large thickness. Here, a 13 μm-thick laminar framework with ≈1.3 nm interlayer channels is fabricated by self-assembling rigid, hydrophilic vermiculite (Vr) nanosheets. Then, Li0.33 La0.557 TiO3 (LLTO) precursors are impregnated in interlayer channels and afterwards in situ sintered to large-size, oriented, and defect-free LLTO crystal. We demonstrate that the confinement effect permits ordered arrangement of LLTO crystal along the c-axis (the fastest Li+ transfer direction), permitting the resultant 15 μm-thick Vr-LLTO electrolyte an ionic conductivity of 8.22×10-5  S cm-1 and conductance of 87.2 mS at 30 °C. These values are several times' higher than that of traditional LLTO-based electrolytes. Moreover, Vr-LLTO electrolyte has a compressive modulus of 1.24 GPa. Excellent cycling performance is demonstrated with all-solid-state Li/LiFePO4 battery.
    [Abstract] [Full Text] [Related] [New Search]