  • Title: Realization of Negative Thermal Expansion in Lead-Free Bi0.5K0.5VO3 by the Suppression of Tetragonality.
    Author: Pan Z, Koike T, Nishikubo T, Hu L, Liu Q, Sakai Y, Kawaguchi S, Azuma M.
    Journal: Inorg Chem; 2022 Feb 28; 61(8):3730-3735. PubMed ID: 35148105.
    Abstract:
    Bi1/2K1/2VO3 is a lead-free PbTiO3-type compound with a tetragonality (c/a = 1.054) comparable to that of typical ferroelectric PbTiO3 (c/a = 1.064) with negative thermal expansion (NTE) during the tetragonal-to-cubic phase transition; therefore, Bi1/2K1/2VO3 is a potential lead-free NTE material if its metastable perovskite structure can be maintained at high temperatures. In the present experiment, electron doping in Bi1/2K1/2VO3 was conducted through substituting K+ with La3+ to suppress the tetragonality and achieve NTE. La substitution successfully suppressed the tetragonality of Bi1/2K1/2VO3 and also improved its thermal stability. Moreover, both composition- and temperature-induced tetragonal-to-cubic phase transitions occurred. In particular, a large volume shrinkage with a large negative thermal coefficient of expansion (CTE) was obtained for Bi0.5K0.46La0.04VO3 during the tetragonal-to-cubic phase transition (ΔV = -0.66%). Hence, this study extends the NTE family and also sheds light on the exploration of lead-free piezoelectric materials with controllable thermal expansion.
    [Abstract] [Full Text] [Related] [New Search]