  • Title: Glucose-mediated one-pot hydrothermal synthesis of hollow magnesium oxide-zinc oxide (MgO-ZnO) microspheres with enhanced natural sunlight photocatalytic activity.
    Author: Vishwanathan S, Das S.
    Journal: Environ Sci Pollut Res Int; 2023 Jan; 30(4):8512-8525. PubMed ID: 35460004.
    Abstract:
    Glucose -mediated one-pot hydrothermal method has been utilized to synthesize hollow spherical MgO-ZnO (xMgO-(1-x)ZnO, x = 0, 0.2, 0.4, 0.6) microstructures which are highly efficient in high-energy ultraviolet (UV) region of natural sunlight. In this process, glucose formed roundish spheres, and simultaneously metal precursors were coated on that spheres during the hydrothermal reaction. X-ray diffraction analysis (XRD) supports the formation of highly crystalline wurtzite structure of MgO-ZnO for Mg loading less than 20%. Higher concentration of Mg produces wurtzite hexagonal ZnO and cubic MgO in the composites. The widening in band gap energy of synthesized MgO-ZnO microspheres compared to ZnO was analyzed by UV-visible diffuse reflectance spectroscopy (UV-DRS) result. Brunauer-Emmett-Teller (BET) surface area analysis showed that with the increase in Mg loading, the specific surface area increases up to 14.27 times as compared to pristine ZnO. The synthesized catalysts were used as an efficient photocatalyst towards the degradation of rhodamine B (RhB), methylene blue (MB), and phenol under natural solar irradiation. Results illustrated that MB and RhB dye solutions were 100% degraded by 0.6 MgO-ZnO in 100 min and 150 min, respectively, whereas pure ZnO samples showed only 65% and 79% degradation. Also, for phenol solution, 0.6 MgO-ZnO showed enhanced degradation efficiency of 72% in 240 min in comparison with 58% degradation shown by ZnO. Additionally, the MgO-ZnO catalysts were stable and showed excellent degradation efficiency up to four consecutive cycles which open a new direction towards potential industrial applications. Hence, the novelty of the current work is to prepare hollow MgO-ZnO microspheres by a single-step hydrothermal process where separate carbon template preparation is not required and to utilize these hollow microspheres as a highly efficient photocatalyst by harnessing the high-energy UV fraction of natural sunlight.
    [Abstract] [Full Text] [Related] [New Search]