  • Title: Adsorptivity and kinetics for low concentration of gaseous formaldehyde on bamboo-based activated carbon loaded with ammonium acetate particles.
    Author: Duan C, Meng M, Huang H, Wang H, Ding H, Zhang Q.
    Journal: Environ Res; 2023 Apr 01; 222():115364. PubMed ID: 36736757.
    Abstract:
    The highly promising formaldehyde (HCHO)-removing materials are essential for eliminating interior pollution to safeguard the public's health with increasing indoor HCHO contamination situations being recorded on a global scale. In the paper, bamboo charcoal (BC) was activated with boric acid to prepare bamboo-based activated carbon (BAC), and then impregnated with ammonium acetate solution to successfully develop porous adsorbent with ammonium acetate particles (N/BAC), which was applied to remove low concentration of HCHO at room temperature. The adsorption performance for HCHO was systematically investigated while the surface chemical properties and microstructure of the as-prepared adsorbents were described and analyzed. The specific surface area, total pore volume and microporous volume of N/BAC sample were 240.09 m2/g, 0.27 cm3/g and 0.12 cm3/g, which increased by 42.40 m2/g, 0.15 cm3/g and 0.03 cm3/g compared with BAC sample, respectively. The specific surface area and the microporous volume, as well as the content of oxygen- and nitrogen-containing functional groups of N/BAC sample were augmented by contrast with other samples, and numerous ammonium acetate particles were present on the surface. Precisely because of this, the N/BAC sample exhibited a high removal rate of 98.89%, which was 18.38% greater than that of BAC sample. A superior correlation coefficient (0.9999) from the experimental values of the kinetics and the fitted values of the pseudo-second-order kinetic model demonstrated that the adsorption process of HCHO on N/BAC sample was physical-chemical combined adsorption. The adsorption of HCHO on N/BAC sample was investigated under different humidity, and the results showed that the adsorbent yet had excellent adsorption capacity (87.93%) under RH 75%. Moreover, the N/BAC sample was renewable, and the removal rate still reached 82.81% after five cycles of regeneration. Therefore, the as-prepared adsorbent is an effective, economical and sustainable material, and could be used to remove HCHO from real contaminated indoor air.
    [Abstract] [Full Text] [Related] [New Search]