  • Title: Graphene-grafted bimetallic MOF membranes for hazardous & toxic contaminants treatment.
    Author: Rehman A, Jahan Z, Khan Niazi MB, Noor T, Javed F, Othman SI, Abukhadra MR, Nawaz A.
    Journal: Chemosphere; 2023 Nov; 340():139721. PubMed ID: 37541443.
    Abstract:
    Development of membrane with improved carbon dioxide (CO2) gas separation capability is a significant challenge. However, the fabrication of membrane that efficiently separate and purification CO2-containing gases has been the focus of global attention. Cellulose Acetate (CA) has robust reinforcing characteristics when incorporated within a suitable polymer matrix. This work focus on the synthesis of novel mixed matrix membranes (MMMs) by introducing Graphene-grafted bimetallic MOFs in Cellulose Acetate polymer. The graphene-grafted bimetallic MOF (GG-BM MOFs) was prepared by a hydrothermal technique. Whereas, the solution casting approach used to fabricate membranes. The 1-5 wt% of GG-BM MOFs incorporated into the CA matrix. The mechanical, hydrophilicity and adsorption characteristics of fabricated MMMs were investigated. The crystallinity of MMM enhanced after the addition of GG-BM MOFs. In addition, the mechanical characteristics of MMMs were improved with the incorporation of GG-BM MOFs inside the polymer matrix. Maximum stress and strain was obtained for 2 wt% MMM (36.4 N/mm2 and 11% respectively). The CO2 adsorption performance was evaluated at 10 bar and 45 °C. The FTIR results represent insignificant bond shifting with the addition GG-BM MOFs at these conditions. The overall results showed that MMMs containing 2 wt% GG-BM MOFs have good adsorption properties for CO2 i.e 3.15 wt% of CO2. The MMMs have shown a decrease in the mechanical properties and CO2 adsorption at the higher GG-BM MOFs loading due to the presence of agglomeration which was confirmed through SEM. Thus, the addition of GG-BM MOFs in the CA matrix positively altered the physicochemical characteristics of the resulting MMMs, which could assist them in achieving remarkable CO2 adsorption at 2 wt%.
    [Abstract] [Full Text] [Related] [New Search]