  • Title: Impingement testing of total hip replacements according to ASTM F2582 - Implant wear, resistance to damage and acceptance criteria.
    Author: Kaddick C, Schmidt C, Grupp TM, Steffens J.
    Journal: J Mech Behav Biomed Mater; 2024 Feb; 150():106270. PubMed ID: 38056402.
    Abstract:
    OBJECTIVES: The aim of this study was to determine the resistance to impingement damage of three different artificially aged UHMWPE materials used for total hip joint replacement. The results obtained can be used as a basis for an acceptance criterion for testing according to ASTM F2582-20. METHODS: Three different polyethylene liner materials, standard polyethylene (UHMWPE), moderately crosslinked (XLPE) and vitamin E stabilized crosslinked (XLPE-VE) polyethylene of the same design and manufacturer were tested up to one million impingement cycles according to ASTM F2582-20. The liners were artificially oxygen aged for two and three weeks according to ASTM F2003-02. The wear volumes of the liner, acetabular shells, and hip endoprosthesis stems were determined. Each of the six impingement test groups consisted of three samples. For each test group, a reference group was subjected to the same conditioning and loading conditions but without impingement between the hip stem and the liner. The force needed to disassemble the liner from the acetabular shell (push-out force) was determined according to ASTM F1820-22 for the test and the reference groups. RESULTS: XLPE and XLPE-VE polyethylene groups showed less impingement wear when compared to the standard UHMWPE material. Similarly, the protective function of the liner against direct metal-on-metal contact was greater, resulting in less wear on the acetabular shell and the stem neck. The three weeks aged standard UHMWPE group showed early onset of fatigue delamination wear. The push-out values remained unchanged for all XLPE liners and the 3-week aged XLPE-VE liners. The aged UHMWPE liners showed low push-out strength due to component shrinkage caused by aging in combination with the tapered fixation used for this specific design. SIGNIFICANCE: The largest polyethylene wear volume measured of XLPE and XLPE-VE polyethylene aged for two and three weeks was 15.05 mm³ (SD 0.56 mm³). The corresponding metal wear volume was 1.23 mm³ (SD 0.19 mm³) for the acetabular cup and 1.33 mm³ (SD 0.20 mm³) for the stem neck. Those values can support the definition of an acceptance criteria for impingement testing. The results of the push-out test required by ASTM F2582-20 should be evaluated with respect to geometry changes caused by aging. The protective effect of the polyethylene liner against metal-on-metal contact should be considered in the implant design phase in order to avoid implant failure due to metal debris.
    [Abstract] [Full Text] [Related] [New Search]