  • Title: Specific contact resistivity reduction in amorphous IGZO thin-film transistors through a TiN/IGTO heterogeneous interlayer.
    Author: Jeong JH, Seo SW, Kim D, Yoon SH, Lee SH, Kuh BJ, Kim T, Jeong JK.
    Journal: Sci Rep; 2024 May 13; 14(1):10953. PubMed ID: 38740958.
    Abstract:
    Oxide semiconductors have gained significant attention in electronic device industry due to their high potential for emerging thin-film transistor (TFT) applications. However, electrical contact properties such as specific contact resistivity (ρC) and width-normalized contact resistance (RCW) are significantly inferior in oxide TFTs compared to conventional silicon metal oxide semiconductor field-effect transistors. In this study, a multi-stack interlayer (IL) consisting of titanium nitride (TiN) and indium-gallium-tin-oxide (IGTO) is inserted between source/drain electrodes and amorphous indium-gallium-zinc-oxide (IGZO). The TiN is introduced to increase conductivity of the underlying layer, while IGTO acts as an n+-layer. Our findings reveal IGTO thickness (tIGTO)-dependent electrical contact properties of IGZO TFT, where ρC and RCW decrease as tIGTO increases to 8 nm. However, at tIGTO > 8 nm, they increase mainly due to IGTO crystallization-induced contact interface aggravation. Consequently, the IGZO TFTs with a TiN/IGTO (3/8 nm) IL reveal the lowest ρC and RCW of 9.0 × 10-6 Ω·cm2 and 0.7 Ω·cm, significantly lower than 8.0 × 10-4 Ω·cm2 and 6.9 Ω·cm in the TFTs without the IL, respectively. This improved electrical contact properties increases field-effect mobility from 39.9 to 45.0 cm2/Vs. This study demonstrates the effectiveness of this multi-stack IL approach in oxide TFTs.
    [Abstract] [Full Text] [Related] [New Search]