  • Title: Additive-Free Anode with High Stability: Nb2CTx MXene Prepared by HCl-LiF Hydrothermal Etching for Lithium-Ion Batteries.
    Author: Zhu X, Yang K, Zhang Z, He S, Shen Z, Jiang W, Huang Y, Xu Y, Jiang Q, Pan L, Li Q, Yang J.
    Journal: ACS Appl Mater Interfaces; 2024 Jun 05; 16(22):28709-28718. PubMed ID: 38780517.
    Abstract:
    MXenes, represented by Ti3C2Tx, have been widely studied in the electrochemical energy storage fields, including lithium-ion batteries, for their unique two-dimensional structure, tunable surface chemistry, and excellent electrical conductivity. Recently, Nb2CTx, as a new type of MXene, has attracted more and more attention due to its high theoretical specific capacity of 542 mAh g-1. However, the preparation of few-layer Nb2CTx nanosheets with high-quality remains a challenge, which limits their research and application. In this work, high-quality few-layer Nb2CTx nanosheets with a large lateral size and a high conductivity of up to 500 S cm-1 were prepared by a simple HCl-LiF hydrothermal etching method, which is 2 orders of magnitude higher than that of previously reported Nb2CTx. Furthermore, from its aqueous ink, the viscosity-tunable organic few-layer Nb2CTx ink was prepared by HCl-induced flocculation and N-methyl-2-pyrrolidone treatment. When using the organic few-layer Nb2CTx ink as an additive-free anode of lithium-ion batteries, it showed excellent cycling performance with a reversible specific capacity of 524.0 mAh g-1 after 500 cycles at 0.5 A g-1 and 444.0 mAh g-1 after 5000 cycles at 1 A g-1. For rate performance, a specific capacity of 159.8 mAh g-1 was obtained at a high current density of 5 A g-1, and an excellent capacity retention rate of about 95.65% was achieved when the current density returned to 0.5 A g-1. This work presents a simple and scalable process for the preparation of high-quality Nb2CTx and its aqueous/organic ink, which demonstrates important application potential as electrodes for electrochemical energy storage devices.