  • Title: Effect of nanodiamonds surface deposition on hydrophilicity, bulk degradation andin-vitrocell adhesion of 3D-printed polycaprolactone scaffolds for bone tissue engineering.
    Author: ElBakry HA, Ammar MM, Moussa TA.
    Journal: Biomed Mater; 2024 Jul 15; 19(5):. PubMed ID: 38917826.
    Abstract:
    This study was designed to deposit nanodiamonds (NDs) on 3D-printed poly-ϵ-caprolactone (PCL) scaffolds and evaluate their effect on the surface topography, hydrophilicity, degradation, andin-vitrocell adhesion compared to untreated PCL scaffolds. The PCL scaffold specimens were 3D-printed by fused deposition modeling (FDM) technique with specific porosity parameters. The 3D-printed specimens' surfaces were modified by NDs deposition followed by oxygen plasma post-treatment using a plasma focus device and a non-thermal atmospheric plasma jet, respectively. Specimens were evaluated through morphological characterization by field emission scanning electron microscope (FESEM), microstructure characterization by Raman spectroscopy, chemical characterization by Fourier transform infrared (FTIR) spectroscopy, hydrophilicity degree by contact angle and water uptake measurements, andin-vitrodegradation measurements (n= 6). In addition,in-vitrobone marrow mesenchymal stem cells adhesion was evaluated quantitatively by confocal microscopy and qualitatively by FESEM at different time intervals after cell seeding (n= 6). The statistical significance level was set atp⩽ 0.05. The FESEM micrographs, the Raman, and FTIR spectra confirmed the successful surface deposition of NDs on scaffold specimens. The NDs treated specimens showed nano-scale features distributed homogeneously across the surface compared to the untreated ones. Also, the NDs treated specimens revealed a statistically significant smaller contact angle (17.45 ± 1.34 degrees), higher water uptake percentage after 24 h immersion in phosphate buffer saline (PBS) (21.56% ± 1.73), and higher degradation rate after six months of immersion in PBS (43.92 ± 0.77%). Moreover, enhanced cell adhesion at all different time intervals was observed in NDs treated specimens with higher nuclei area fraction percentage (69.87 ± 3.97%) compared to the untreated specimens (11.46 ± 1.34%). Surface deposition of NDs with oxygen-containing functional groups on 3D-printed PCL scaffolds increased their hydrophilicity and degradation rate with significant enhancement of thein-vitrocell adhesion compared to untreated PCL scaffolds.
    [Abstract] [Full Text] [Related] [New Search]