  • Title: Effects of titanium nitride coatings on surface and corrosion characteristics of Ni-Ti alloy.
    Author: Endo K, Sachdeva R, Araki Y, Ohno H.
    Journal: Dent Mater J; 1994 Dec; 13(2):228-39. PubMed ID: 7758284.
    Abstract:
    The structure of a titanium nitride film coated by arc ion plating on a Ni-50Ti shape memory alloy was characterized by X-ray photoelectron spectroscopy (XPS). The corrosion behavior of the titanium nitride-coated Ni-50Ti alloy was examined in 0.9% NaCl solution by potentiodynamic polarization measurements and a polarization resistance method. XPS spectra showed that the titanium nitride film consisted of three layers, a top layer of TiO2, a middle layer of TiNx (x > 1), and an inner layer of TiN. The passive current density for the titanium nitride-coated alloy was approximately two orders of magnitude lower than that of the polished alloy in the potential range from the free corrosion potential to +500 mV (vs. Ag/AgCl). Pitting corrosion associated with breakdown of the coated film occurred above this potential. The polarization resistance data also indicated that the corrosion rate of the titanium nitride-coated alloy at the free corrosion potential (+50-+100 mV) was more than one order of magnitude lower than that for the polished alloy.
    [Abstract] [Full Text] [Related] [New Search]