  • Title: A pilot study of the marginal adaptation and surface morphology of glass-cermet cements.
    Author: Chu CH, King NM, Lee AM, Yiu CK, Wei SH.
    Journal: Quintessence Int; 1996 Jul; 27(7):493-501. PubMed ID: 8941827.
    Abstract:
    This study investigated changes in the marginal adaptation and surface morphology of Ketac-Silver and Chelon-Silver glass-current cements over time. Dispersalloy amalgam was used as a control. Contralateral pairs of carious primary molars were restored with the test materials and amalgam. Clinical evaluations were scheduled at 12, 18, and 24 months after placement. Gold-plated replicas of the restorations were observed with scanning electron microscopy. Fractures and cracks in the surface of the Dispersalloy and Chelon-Silver increased the surface roughness; however, the damage was superficial and self-limiting in the Dispersalloy restorations, while in Chelon-Silver the fractures caused the material to break down in layers. A substantial quantity of pores, usually smaller than 50 microns in diameter, were observed throughout the surface of the Chelon-Silver restorations. The pores in the surface of Ketac-Silver were fewer and smaller. The incidence of cavomarginal breakdown increased with time. Chelon-Silver restorations had a higher rate of cavomarginal breakdown than did Ketac-Silver and Dispersalloy restorations up to 18 months. However, there was no statistically significant difference in the marginal adaptation of the three groups at 24 months.
    [Abstract] [Full Text] [Related] [New Search]