  • Title: Brushing abrasion of eroded dentin after application of sodium fluoride solutions.
    Author: Attin T, Zirkel C, Hellwig E.
    Journal: Caries Res; 1998; 32(5):344-50. PubMed ID: 9701659.
    Abstract:
    The aim of the present in vitro study was to evaluate the influence of sodium fluoride solutions on brushing abrasion of eroded dentin. Dentin specimens were prepared from 60 bovine incisors. The specimens were embedded in acrylic resin, ground flat, polished and subsequently covered with tape exposing an area of 1.8 mm x 10.0 mm in the center of the exposed dentin. The samples were alternatingly stored in a demineralizing solution (5 min) and a remineralizing solution (1 min) for 5 times. The erosive soft drink Sprite light(R) served as a demineralizing solution and artificial saliva was used as a remineralizing solution. Prior to storage in artificial saliva 15 specimens were each treated for 1 min with 250 and 2,000 ppm fluoride solution, respectively. Fifteen specimens were treated with distilled water instead of the fluoride solution (= eroded controls). The remaining samples were neither eroded with the soft drink nor fluoridated (= uneroded controls). After each immersion in artificial saliva the specimens were submitted to abrasion in a toothbrushing machine. After 5 demineralization-remineralization brushing cycles the total amount of tooth wear due to erosion and subsequent abrasion was profilometrically evaluated. Statistical analysis revealed the significantly lowest wear in the uneroded controls and the highest amount of abrasion in the eroded controls. Application of the fluoride solutions increased the wear resistance of the eroded dentin specimens, showing significantly better protection by the high-concentration compared to the low-concentration solution. The susceptibility to abrasion of the eroded dentin specimens treated with the high-concentration fluoride solution did not differ significantly from the uneroded dentin samples. It is concluded that application of 2,000 ppm sodium fluoride solutions immediately before toothbrushing significantly reduces abrasion of eroded dentin in vitro.
    [Abstract] [Full Text] [Related] [New Search]